Green Synthesis of Cellulose Graft Copolymers for Anion Exchange Water Purification

1 online resource (100 pages) : PDF

2022

University of North Carolina at Charlotte

This thesis describes the synthesis and characterization of novel cellulose graft copolymers that are used for the purification of drinking water. These nanomaterials function as bottle-brush anion-exchange resins with repeating quaternary ammonium polyelectrolyte chains covalently coupled to a cellulose scaffolding. In the synthesis process of cellulose nanoresin (CNR), commercial microcrystalline cellulose is oxidized at the C-6 position to form cellouronic acid via the (2,2,6,6-tetramethylpiperidin-1-yl)oxidanyl (TEMPO) radical while under sonication, or high-pressure homogenization. Polyelectrolyte chains are then synthesized with controlled strand lengths using the ARGET-ATRP mechanism. CNR was prepared in all-aqueous medium by Fischer-Speier esterification using a catalytic amount of hydrochloric acid. Carboxyl contents of TEMPO-oxidized nanocellulose (TONC) and of CNR were measured using conductometric titration, with values as high as 1.61 mmol g-1 for TONC and as low as 0.627 mmol g-1 for CNR respectively. Percent functionalization of CNR was calculated to be 61%. The hydrodynamic diameter and zeta potential of TONC and CNR were measured by dynamic light scattering (DLS). DLS data showed a decrease in the size of the particles in dispersion after the oxidation of cellulose. Consistent with our graft copolymer model, the particle’s size increased after polyelectrolyte functionalization. The surface charge of dispersed particles of commercial cellulose, TONC, and CNR also changed from neutral to negative to positive at pH 7, indicating successful synthetic procedures. CNR was further characterized by testing its functionality as a thin-film membrane and as an adsorbent material for anion exchange applications. CNR membranes were found to exhibit high water flux of >700 L m-2 h-1 bar-1 and high loading capacities of >20 mg g-1 when tested using a sodium fluorescein (NaFL) surrogate adsorbate. These materials exhibit fast kinetics, with equilibrium loading being achieved in a matter of seconds. CNR thin films are regenerable and reusable as water purification membranes, with a decrease in loading capacity of only 0.01 ± 0.01 mg NaFL per gram of CNR, or 0.03% after 40 cycles.

masters theses

Chemistry

M.S.

Cellulose
Functionalized Polymers
Green Chemistry
Ion-Exchange
Nanomaterials
Water Purification

Chemistry

Poler, Jordan

Troutman, Jerry
Cooper, Brian
Jacobs, Donald

Thesis (M.S.)--University of North Carolina at Charlotte, 2022.

This Item is protected by copyright and/or related rights. You are free to use this Item in any way that is permitted by the copyright and related rights legislation that applies to your use. For other uses you need to obtain permission from the rights-holder(s). For additional information, see http://rightsstatements.org/page/InC/1.0/.

Copyright is held by the author unless otherwise indicated.

Schmal_uncc_0694N_13224

http://hdl.handle.net/20.500.13093/etd:3093